Ultra white clear float glass manufacturer for Building Toughened Triple PVB Low-E Laminated Glass

Ultra white clear float glass manufacturer for Building Toughened Triple PVB Low-E Laminated Glass

Ultra Clear Medium Aluminosilicate Electronic Float Glass(CHIYAN-M2) is an eco-friendly ultra clear alumino-silicate glass with certain strength.

Glass Type: Float glass

For float glass, due to the thickness uniformity is better, the transparency of the product is also relatively strong, because after the tin surface treatment, relatively smooth, under the action of surface tension, formed a surface is relatively neat, flatness is relatively good, optical performance is relatively strong glass, the decorative characteristics of this float glass is particularly good. More with good transparency, brightness, purity, and bright indoor light characteristics, broad field of vision performance, but also with building doors and Windows, natural lighting materials of the best choice of materials, but also one of the most highly applied building materials, it can be said that in a variety of architectural glass, this float glass application is the largest, It is one of the most important raw pieces for glass deep processing. Ultra-white float glass has the best transparency and purity as its main feature.

Standard shipping Size:1300*1100mm (5th Generation)

Regular Thickness:

2.0mm 1.80mm 1.50mm 1.30mm

1.10mm 0.70mm 0.55mm

0.40mm 0.33mm 0.25mm

Note: The size can be customized according to customer's needs.

Features:

High Bending Strength Resistance

High Impact Resistance

High Scratch Resistance

High Flexibility

CHIYAN-M2’s 0.25~2.0mm thickness medium alumino-silicate glass has already been used in the market to meet a wide range of customers needs.

Application:
1. Architecture, such as windows or other areas in a building
2. Traffic vehicles, such as the windows of train, bus, car etc
3. Household appliances and furniture, such as glass table top and show shelves.

Product Composition

Ultra Clear Medium Aluminosilicate Glass achieves better stress and strain depth than ordinary soda-lime glass by increasing the Al₂O₃ content in the glass and increasing the ion exchange capacity.

Chemical Tempering Process Parameter Setting Reference

Note: Tempering solution Na+<0.5%. The above test results are affected by processing conditions, the data is for reference only, not as a basis for production.

Dimensions

NO.	Item	Specification	Detection Method
1	Dimensional Tolerance	1300*1100*(±2mm)	Tape Measure
2	Thickness	0.50~1.1 ±0.05m 1.3~2.0 ±0.05m	Micrometer
3	Thickness Difference	≤0.04mm	Micrometer
4	The Diagonal Difference (Perpendicularity)	≤0.3%	Tape Measure
5	Stripe	≤Level2	Point Sources of Light
6	Flatness (Before Tempering)	0.50~0.55 ≤0.15%(=h/L) 0.70~2.0 ≤0.10%(=h/L)

Appearance descriptions

NO.	Item		Specification	Detection Method
1	Effective Mass Area		All areas outside 10mm of the edge are effective mass areas.
2	Appearance Defects	Scratches	w≤0.03mm, Allowed 0.03mm＜w≤0.05mm,L≤25mm (Controlled by point defects) w＞0.05mm, Not allowed	Fluorescent Lamp 2000-2500Lux
		Bubbles	d≤0.05mm, Not counted 0.05mm＜d≤0.2mm, Numbers≤5 /m² d＞0.2mm,Not allowed
		Inclusions such as stones and sticky tin	d≤0.05mm, Not counted 0.05mm＜d≤0.2mm, Numbers≤5 /m² d＞0.2mm,Not allowed
3	Edge Defects	Chipping	Single chipping L≤2.0mm,W≤1.0mm,D≤1/2 of the thickness (as the right picture showed). The cumulative length of chipping is less than 10% of the edge length of the glass plate.
4		Cracks and missing corners	Not allowed
5	Surface stains (glass shavings, attachments, point contamination)		No stains that cannot be removed by ordinary detergents are allowed.
			d≤0.05mm, Not counted 0.05mm＜d≤0.3mm, Numbers≤5 /m² d＞0.3mm,Not allowed	The same method as appearance detection.

Packing Quantity

Packaging Diagram

Storage
Storage conditions: Temperature ≤30℃, humidity ≤65% (no condensation), shelf life is 6 months from the date of delivery.

Float glass is made by heating raw materials—silica sand, limestone, soda ash, and magnesium in a furnace. When melted, it’s then spread out over a sizable bed of molten tin. As it moves along rollers in the annealing oven during a controlled cooling process, this mixture slowly solidifies over the molten tin. From this point, a single, continuous smooth ribbon of glass emerges as below picture showed: